Performance
- M-ES806 Epoxy Adhesive for Stone Material is a two component
high modulus structural epoxy paste adhesive. It's interlinked
to produce high adhesive strength at room temperature (at
25 degree c)
- M-ES806 is a two-component structural epoxy paste adhesive
for construction with advantages of high bonding strength
and fast hardening, heat, cold, water and aging resistance.
It is widely used in many applications, such as install
of curtain wall epoxy adhesive, bonding of metal structures
and repair of stone materials, as well as adhesion of materials
(e.g.stones, ceramics, cement, glass, etc.)
Typical products properties:
Blend at mixing ratio thoroughly
| Induction period(minutes)
|
15-25 |
| Flexural elastic modulus (MPa) |
3000 |
Tensile-shear strength(stainless steel-stainless steel)(MPa)
|
>=10
|
Compressive shear strength:stone-stainless steel
| Standard conditions
48h(MPa)(must meet technical requirement by jc 897-2001
standard) |
13.5 |
Compressive shear strength:stone---stone
| Standard conditions
48h(MPa) |
14.5 |
| Wetting 168(MPa) |
>=10
|
| Heat treatment 168(Mpa) |
>=10
|
Freeze thaw 50 cycles(MPa)
|
>=9 |
|
|
Usage
M-ES806 is a two-component structural epoxy paste adhesive
for construction. The surfaces must be cleaned and keep dry
before the adhesive is applied. For metal, rust and plated
zinc must be removed; for slate, smooth surface must be roughened.
Mix M-ES806 at ration of A:B=1:1(weight) and apply it to both
surfaces to be boned forcibly for the strongest adhesion.
Induction period is 15 minutes (at 25¢J) from two components
mixing, which is shorter at high temperature.
Storage and Shelf Life:12 month; two components should store
separately in a dry ventilated place.
|